Product
| Description | Features/Advantages | Applicable Resin System | Adding Method And Amount | Applicable Diluent |
| Silane Coupling Agent |
| XIAMETER™6011 Silane | Aminopropyltriethoxysilane; 99% active | Adhesion promoter in waterborne and solventborne coatings and pigment treatment in waterborne coatings | Waterborne and solventborne acrylic; solventborne polyurethane; 2K acrylic epoxy for concrete and industrial maintenance | Add when grinding or painting, or add after. 0.05 to 2.0% | Alcohol and water |
| XIAMETER™6020 Silane | Aminoethylaminopropyltrimethoxysilane; 99% active | Adhesion promoter and pigment treatment in waterborne and solventborne coatings | Waterborne and solventborne acrylic, alkyd, epoxy, polyurethane | Can be added when grinding or dispensing paint. Primer diluted to 10% in isopropyl alcohol Additive active content: 0.5-2.0% | Alcohol and water |
| XIAMETER™6030 Silane | 3-methacryloxypropyltrimethoxysilane; 98% active | Improves adhesion of waterborne, solventborne and radiation-cured coatings to inorganic substrates when used as a primer or additive | Waterborne and solventborne acrylic, alkyd, epoxy, polyester, polyurethane, vinyl; radiation-cured acrylic | Add when mixing paint, or add afterward. Primer: dilute 0.1-0.5% in acidic (PH~4.0) water. Active additive: 0.1-3.0% | Alcohol and water |
| XIAMETER™6032 Silane | Cationic vinylbenzyl and aminofunctional methoxy-silane; 40% active | Adhesion promoter in waterborne and solventborne coatings; can be used as an additive or primer | Waterborne and solventborne acrylic, epoxy | It can be added during grinding or paint preparation, or added afterward. Primer: Dilute with a 10:1 mixture of methanol or ethanol and water. Active additive: 0.05-3.0wt% | Alcohol and water |
| XIAMETER™6040 Silane | Glycidoxypropyltrimethoxysilane; 99% active | Adhesion promoter and pigment treatment in waterborne and solventborne coatings; can be used as an additive or primer | Waterborne and solventborne acrylic, alkyd, amine, epoxy, polyurethane, vinyl | Can be added during grinding or paint preparation. Primer: dilute to 10% in isopropyl alcohol, active content additive: 0.05-3.0% | Alcohol and water |
| XIAMETER™6070 Silane | Low viscosity alkoxysilane, effective content 95% | Used as surface hydrophobic agent for inorganic materials and pigment dispersant. | It reacts with water to generate silanol and methanol. Silanol can condense with the carboxyl groups on the surface of inorganic materials such as quartz, clay, and silica to form a hydrophobic layer. | As a pigment and filler treatment agent, the added amount is 0.5-1.0% of the total solid content; powder filler treatment can be added directly to the powder mixer. When used as diluent, dilute 10% with methanol or isopropanol. | Methanol, isoalcohol and water |
| XIAMETER™6062 Silane | Mercaptopropyl functional trimethoxy-silane, effective content 98%. | Provides coupling between inorganic surfaces (clay, glass) and sulfur-cured elastomers, improving the physical properties of mineral elastomers. | UV resin, modified filled elastomer, metal aluminum substrate adhesion promoter | Alkoxysilane hydrolyzes into methanol when combined with water | Alcohol and water |
| XIAMETER™6697 Silane | Ethyl orthosilicate (TEOS), effective content 99%. | The small molecule structure has good permeability and is combined with inorganic, high anti-ultraviolet stability, does not affect the aesthetics of the substrate, maintains water vapor penetration, and can undergo sol-gel reaction with OFS-6070. | Stone reinforcement for construction materials such as buildings or monuments. | Use alone, diluted, or used in formulated products containing 70-75% active ingredient | Alcohol and water |
| XIAMETER™6403 Silane | Undiluted high purity isobutyltriethoxysilane with an effective content of 98%. | The small molecular structure can penetrate deeply into the concrete surface to produce a water-repellent treatment layer, inhibit water absorption, and help surface modification improve compatibility with non-polar substrates. | Water-based or inorganic resins. | Seal gun, roller, brush, reapply, thoroughly soaked | Isopropyl alcohol, ethanol or various flash point solvent oils |
| XIAMETER™6341 Silane | High purity undiluted (n-octyltriethoxysilane), effective content 98%. | The small molecular structure can penetrate deeply into the concrete surface to produce a water-repellent treatment layer, improve the dispersion of polar fillers in non-polar materials, and can be used to formulate waterproofing products. | Oily or inorganic resins. | Seal gun, roller, brush, reapply, thoroughly soaked.The solvent contains 20% and 40% silane | Alcohol, chlorinated solvent, aliphatic solvent, low molecular weight polydimethylcyclosiloxane |
| XIAMETER™6124 Silane | Inorganic surface hydrophobic arylalkoxysilane, effective content 94%. | It has inorganic reactivity, can achieve inorganic surface hydrophobicity, and can be used for pigment treatment. It is a silane coupling agent mixture. | - | Surface silylation: 2% Silane solution, primer: 3.5-4% Pigments and fillers: 0.5-1.0% Additive: 0.1-3.0% | Methanol, ethanol, isopropyl alcohol, acetic acid |
| XIAMETER™6778 Silane | Water-soluble potassium methyl silicate salt solution, effective content 40%. | As a surface treatment agent, it can make the surface of the substrate waterproof and reduce the water absorption of the substrate, making various substrates waterproof.Colorless and non-yellowing, it maintains its original appearance. | -
| Dilute to 3% or less Dip, spray or brush |
Water |
| XIAMETER™6610 Silane | High purity amino functional alkoxysilane, effective content 98.5%. | Improve the dry and wet, tensile/flexural strength and modulus of composite materials, increase the transparency of glass fiber materials, and improve the adhesion of plastic resins and elastomers to the surface of inorganic materials. | - | Dilute aqueous solution (0.1-0.5% silicone) | Isopropyl alcohol and water |
| DOWSIL™6132 Silane | The effective content of vinylbenzyl aminoethyl aminopropyl trimethoxysilane (average structure) is 37% | Improve the stickiness of plastic resin to inorganic surfaces, improve the wet strength and dry strength of the composite, and the treated glass fiber fabric has good resin wettability. | Water-based and plastic resin mineral fillers can be used as coupling agents for glass fiber fabrics in printed circuit board composite materials. They can be matched with a variety of organic and inorganic materials to improve the performance of composite materials. | Dilute aqueous solution (silane concentration 0.1-0.5%) on inorganic surfaces | Organic solvents and water |
| DOWSIL™6269 Silane | Styryl-aminotrimethoxy-silane, 40% silane in methanol solution | Improves the adhesion between epoxy resin and inorganic substances (glass fiber), has both organic and inorganic reactivity, and has low turbidity in aqueous solutions. | In printed circuit board composite materials, it is used as a coupling agent between glass fiber cloth and epoxy resin. | After pre-hydrolysis, the recommended concentration is 0.1-0.5wt% silane effective content in aqueous solution | Glacial acetic acid and water |
| DOWSIL™AZ-720 Silane | Amino-functional silane coupling agents and organic polymers | Glass fiber reinforced composites to improve mechanical properties and surface appearance. | Thermoplastic and thermosetting resin fiberglass composite materials | - | - |